ASTM-W1C-10
C(%) | Si(%) | Mn(%) | P(%) | S(%) | Ni(%) | Cr(%) | Mo(%) | W(%) | V(%) | Cu(%) |
---|---|---|---|---|---|---|---|---|---|---|
C(%)(%) 1.0-1.1 | Si(%)(%) 0.1-0.4 | Mn(%)(%) 0.1-0.4 | P(%)(%) ≦0.03 | S(%)(%) ≦0.03 | Ni(%)(%) ≦0.2 | Cr(%)(%) ≦0.3 | Mo(%)(%) ≦0.1 | W(%)(%) ≦0.3 | V(%)(%) ≦0.1 | Cu(%)(%) ≦0.2 |
Aplicaciones
- Acero de herramientas de carbono
Otros
- Annealing HB : ≦202
- Quenching HRC : ≧65