DIN-13CrMo4-4
C(%) | Si(%) | Mn(%) | P(%) | S(%) | Cr (%) | Mo (%) | Cu (%) | Dikte (mm) | Vloeigrens (Mpa) | Treksterkte (Mpa) |
---|---|---|---|---|---|---|---|---|---|---|
C(%)(%) 0,08-0,18 | Si(%)(%) 0,1-0,4 | Mn(%)(%) 0,40-1,00 | P(%)(%) ≦0.035 | S(%)(%) ≦0.03 | Cr (%)(%) 0.70-1.15 | Mo (%)(%) 0.4-0.6 | Cu (%)(%) ≦0,3 | Dikte (mm)(%) ≦16 | Vloeigrens (Mpa)(%) ≧300 | Treksterkte (Mpa)(%) 440-590 |
Toepassingen
- Chroom-Molybdeen Legeringsstaalplaten voor Drukvaten
Landcode
- DIN
Standaard
- 17155
Staaltype
- 13CrMo4-4
Gerelateerd Staaltype
Staaltype | Standaard | Landcode | Meer | SCMV2 | 10716 | CNS | Meer | SCMV2-1 | G4109 | JIS | Meer | SCMV2-2 | G4109 | JIS | Meer | Gr.12 | A387 | ASTM | Meer | 13CrMo4-4 | 17155 | DIN | Meer | SCMV1 | 10776 | CNS | Meer | SCMV1-1 | G4109 | JIS | Meer | SCMV1-2 | G4109 | JIS | Meer | Gr.2 | A387 | ASTM | Meer |
---|