DIN-42CrMoV4
C(%) | Si(%) | Mn(%) | P(%) | S(%) | Cr (%) | Mo (%) | Dikte (mm) | Vloeigrens (Mpa) | Treksterkte (Mpa) | Rekbaarheid (%) |
---|---|---|---|---|---|---|---|---|---|---|
C(%)(%) 0.30-0.45 | Si(%)(%) 0.15-0.40 | Mn(%)(%) 0.5-0.8 | P(%)(%) ≦0,025 | S(%)(%) ≦0,025 | Cr (%)(%) 0.9-1.2 | Mo (%)(%) 0.15-0.30 | Dikte (mm)(%) 16≦t≦40 | Vloeigrens (Mpa)(%) ≧765 | Treksterkte (Mpa)(%) 980-1180 | Rekbaarheid (%)(%) ≧11 |
Toepassingen
- Legeringsstaal Staven voor Speciale Toepassing Bevestigingsmaterialen
Landcode
- DIN
Standaard
- 17240
Staaltype
- 42CrMoV4
Gerelateerd Staaltype
Staaltype | Standaard | Landcode | Meer | SNB22-5 | G4108 | JIS | Meer | Gr.B22-5 | A540 | ASTM | Meer | 42CrMoV4 | 17240 | DIN | Meer | SNB22-4 | G4108 | JIS | Meer | Gr.B22-4 | A540 | ASTM | Meer | SNB22-3 | G4108 | JIS | Meer | Gr.B22-3 | A540 | ASTM | Meer | SNB22-2 | G4108 | JIS | Meer | Gr.B22-2 | A540 | ASTM | Meer | SNB22-1 | G4108 | JIS | Meer | Gr.B22-1 | A540 | ASTM | Meer |
---|