C(%) | Si(%) | Mn(%) | P(%) | S(%) | Ni (%) | Cr (%) | V(%) | Cu (%) | Al(%) | Ti (%) | Dikte (mm) | Vloeigrens (Mpa) | Treksterkte (Mpa) |
---|---|---|---|---|---|---|---|---|---|---|---|---|---|
C(%)(%) ≦0,16 | Si(%)(%) ≦0,35 | Mn(%)(%) 0,40-1,20 | P(%)(%) ≦0.035 | S(%)(%) ≦0.035 | Ni (%)(%) ≦0.30 | Cr (%)(%) ≦0.25 | V(%)(%) ≦0.03 | Cu (%)(%) ≦0.03 | Al(%)(%) ≦0.02 | Ti (%)(%) ≦0.03 | Dikte (mm)(%) ≦16 | Vloeigrens (Mpa)(%) ≧235 | Treksterkte (Mpa)(%) 350-470 |
Toepassingen
- Koolstofstaal en molybdeenlegering staalplaten voor ketels en andere drukvaten