JIS-SCH22
C(%) | Si(%) | Mn(%) | P(%) | S(%) | Ni (%) | Cr (%) | Mo (%) | Vloeigrens (Mpa) | Treksterkte (Mpa) | Rekbaarheid (%) |
---|---|---|---|---|---|---|---|---|---|---|
C(%)(%) 0,35-0,45 | Si(%)(%) ≦1,75 | Mn(%)(%) ≦1.5 | P(%)(%) ≦0.04 | S(%)(%) ≦0.04 | Ni (%)(%) 19.0-22.0 | Cr (%)(%) 23,0-27,0 | Mo (%)(%) ≦0,5 | Vloeigrens (Mpa)(%) ≧235 | Treksterkte (Mpa)(%) ≧440 | Rekbaarheid (%)(%) ≧8 |
Toepassingen
- Hittestand staal gietstukken
Landcode
- JIS
Standaard
- G5122
Staaltype
- SCH22
Gerelateerd Staaltype
Staaltype | Standaard | Landcode | Meer | SCH22 | 4002 | CNS | Meer | ZG40Cr25-Ni20 | 8492 | GB | Meer | SCH22 | G5122 | JIS | Meer | HK40 | A351 | ASTM | Meer | G-X40Cr-NiSi25-20 | 17465 | DIN | Meer |
---|