JIS-SKD4
C(%) | Si(%) | Mn(%) | P(%) | S(%) | Ni (%) | Cr (%) | W (%) | V(%) | Cu (%) |
---|---|---|---|---|---|---|---|---|---|
C(%)(%) 0.25-0.35 | Si(%)(%) ≦0.4 | Mn(%)(%) ≦0.6 | P(%)(%) ≦0.03 | S(%)(%) ≦0.03 | Ni (%)(%) ≦0.25 | Cr (%)(%) 2.0-3.0 | W (%)(%) 5.0-6.0 | V(%)(%) 0,35-0,50 | Cu (%)(%) ≦0.25 |
Toepassingen
- Legerings gereedschapsstalen(2)
Overig
- Annealing HB : ≦235
- Quenching HRC : ≧42
Landcode
- JIS
Staaltype
- SKD4
Gerelateerd Staaltype
Staaltype | Landcode | Meer | SKD4 | CNS | Meer | SKD4 | JIS | Meer | X30WCr-V5-3 | DIN | Meer |
---|