JIS-SKD7
C(%) | Si(%) | Mn(%) | P(%) | S(%) | Ni (%) | Cr (%) | Mo (%) | V(%) | Cu (%) |
---|---|---|---|---|---|---|---|---|---|
C(%)(%) 0,28-0,38 | Si(%)(%) ≦0,5 | Mn(%)(%) ≦0.6 | P(%)(%) ≦0.03 | S(%)(%) ≦0.03 | Ni (%)(%) ≦0.25 | Cr (%)(%) 2.5-3.5 | Mo (%)(%) 2.5-3.0 | V(%)(%) 0.4-0.7 | Cu (%)(%) ≦0.25 |
Toepassingen
- Legerings gereedschapsstalen(2)
Overig
- Annealing HB : ≦229
- Quenching HRC : ≧46