JIS-SKD8
C(%) | Si(%) | Mn(%) | P(%) | S(%) | Ni (%) | Cr (%) | Mo (%) | W (%) | V(%) | Cu (%) |
---|---|---|---|---|---|---|---|---|---|---|
C(%)(%) 0,35-0,45 | Si(%)(%) ≦0,5 | Mn(%)(%) ≦0.6 | P(%)(%) ≦0.03 | S(%)(%) ≦0.03 | Ni (%)(%) ≦0.25 | Cr (%)(%) 4.0-4.7 | Mo (%)(%) 0.3-0.5 | W (%)(%) 3,8-4,5 | V(%)(%) 1.7-2.2 | Cu (%)(%) ≦0.25 |
Toepassingen
- Legerings gereedschapsstalen(2)
Overig
- Co : 3.8-4.5
- Annealing HB : ≦262
- Quenching HRC