ASTM-W1A-10
C(%) | Si(%) | Mn(%) | P(%) | S(%) | Ni(%) | Cr(%) | Mo(%) | W(%) | V(%) | Cu(%) |
---|---|---|---|---|---|---|---|---|---|---|
C(%)(%) 1.0-1.1 | Si(%)(%) 0.1-0.4 | Mn(%)(%) 0.1-0.4 | P(%)(%) ≦0.03 | S(%)(%) ≦0.03 | Ni(%)(%) ≦0.2 | Cr(%)(%) ≦0.15 | Mo(%)(%) ≦0.1 | W(%)(%) ≦0.15 | V(%)(%) ≦0.1 | Cu(%)(%) ≦0.2 |
Uygulamalar
- Karbon Alet Çelikleri
Diğer
- Annealing HB : ≦202
- Quenching HRC : ≧65
Ülke Kodu
- ASTM
Çelik Türü
- W1A-10
İlgili Çelik Türü
Çelik Türü | Ülke Kodu | Daha | SK4 | CNS | Daha | T10 | GB | Daha | SK3 | JIS | Daha | SK4 | JIS | Daha | W1A-10 | ASTM | Daha | W1C-10 | ASTM | Daha | W1A-91/2 | ASTM | Daha | W1C-91/2 | ASTM | Daha | W2A-91/2 | ASTM | Daha | W2C-91/2 | ASTM | Daha | C105W1 | DIN | Daha | C105W2 | DIN | Daha |
---|