ASTM-W1A-8
C(%) | Si(%) | Mn(%) | P(%) | S(%) | Ni(%) | Cr(%) | Mo(%) | W(%) | V(%) | Cu(%) |
---|---|---|---|---|---|---|---|---|---|---|
C(%)(%) 0.8-0.9 | Si(%)(%) 0.1-0.4 | Mn(%)(%) 0.1-0.4 | P(%)(%) ≦0.03 | S(%)(%) ≦0.03 | Ni(%)(%) ≦0.2 | Cr(%)(%) ≦0.15 | Mo(%)(%) ≦0.1 | W(%)(%) ≦0.15 | V(%)(%) ≦0.1 | Cu(%)(%) ≦0.2 |
Uygulamalar
- Karbon Alet Çelikleri
Diğer
- Annealing HB : ≦202
- Quenching HRC : ≧65
Ülke Kodu
- ASTM
Çelik Türü
- W1A-8