DIN-S 2-9-2
C(%) | Si(%) | Mn(%) | P(%) | S(%) | Cr(%) | Mo(%) | W(%) | V(%) |
---|---|---|---|---|---|---|---|---|
C(%)(%) 0.97-1.07 | Si(%)(%) ≦0.45 | Mn(%)(%) ≦0.4 | P(%)(%) ≦0.03 | S(%)(%) ≦0.03 | Cr(%)(%) 3.5-4.2 | Mo(%)(%) 8.0-9.2 | W(%)(%) 1.5-2.0 | V(%)(%) 1.8-2.2 |
Uygulamalar
- Yüksek Hızlı Alet Çelikleri
Diğer
- Annealing HB : 780-810
- Quenching HRC : ≧64
Ülke Kodu
- DIN
Çelik Türü
- S 2-9-2
İlgili Çelik Türü
Çelik Türü | Ülke Kodu | Daha | SKH58 | CNS | Daha | W2Mo9-Cr4V2 | GB | Daha | SKH58 | JIS | Daha | M7 | ASTM | Daha | S 2-9-2 | DIN | Daha |
---|