JIS-SKH4
C(%) | Si(%) | Mn(%) | P(%) | S(%) | Ni(%) | Cr(%) | W(%) | V(%) | Cu(%) |
---|---|---|---|---|---|---|---|---|---|
C(%)(%) 0.73-0.83 | Si(%)(%) ≦0.4 | Mn(%)(%) ≦0.4 | P(%)(%) ≦0.03 | S(%)(%) ≦0.03 | Ni(%)(%) ≦0.25 | Cr(%)(%) 3.8-4.5 | W(%)(%) 17.0-19.0 | V(%)(%) 1.0-1.5 | Cu(%)(%) ≦0.25 |
Uygulamalar
- Yüksek Hızlı Alet Çelikleri
Diğer
- Co : 9.0-11.0
- Annealing HB : ≦285
- Quenching HRC
Ülke Kodu
- JIS
Çelik Türü
- SKH4
İlgili Çelik Türü
Çelik Türü | Ülke Kodu | Daha |
SKH4 |
CNS | Daha |
W18Cr4-V2Co8 |
GB | Daha |
SKH4 |
JIS | Daha |
T5 |
ASTM | Daha |
S 18-1-2-10 |
DIN | Daha |
---|