ASTM-W1A-91/2
C(%) | Si(%) | Mn(%) | P(%) | S(%) | Ni(%) | Cr(%) | Mo(%) | W(%) | V(%) | Cu(%) |
---|---|---|---|---|---|---|---|---|---|---|
C(%)(%) 0,95-1,05 | Si(%)(%) 0,1-0,4 | Mn(%)(%) 0,1-0,4 | P(%)(%) ≦0,03 | S(%)(%) ≦0,03 | Ni(%)(%) ≦0,2 | Cr(%)(%) ≦0,15 | Mo(%)(%) ≦0.1 | W(%)(%) ≦0,15 | V(%)(%) ≦0.1 | Cu(%)(%) ≦0,2 |
Anwendungen
- Kohlenstoff-Werkzeugeisen
Sonstiges
- Annealing HB : ≦202
- Quenching HRC : ≧65
Ländercode
- ASTM
Stahltyp
- W1A-91/2
Stahltyp in Beziehung setzen
Stahltyp | Ländercode | Mehr | SK4 | CNS | Mehr | T10 | GB | Mehr | SK3 | JIS | Mehr | SK4 | JIS | Mehr | W1A-10 | ASTM | Mehr | W1C-10 | ASTM | Mehr | W1A-91/2 | ASTM | Mehr | W1C-91/2 | ASTM | Mehr | W2A-91/2 | ASTM | Mehr | W2C-91/2 | ASTM | Mehr | C105W1 | DIN | Mehr | C105W2 | DIN | Mehr |
---|