ASTM-W2A-91/2
C(%) | Si(%) | Mn(%) | P(%) | S(%) | Ni(%) | Cr(%) | Mo(%) | W(%) | V(%) | Cu(%) |
---|---|---|---|---|---|---|---|---|---|---|
C(%)(%) 0,95-1,10 | Si(%)(%) 0,1-0,4 | Mn(%)(%) 0,1-0,4 | P(%)(%) ≦0,03 | S(%)(%) ≦0,03 | Ni(%)(%) ≦0,2 | Cr(%)(%) ≦0,15 | Mo(%)(%) ≦0.1 | W(%)(%) ≦0,15 | V(%)(%) 0,15-0,35 | Cu(%)(%) ≦0,2 |
Anwendungen
- Kohlenstoff-Werkzeugeisen
Sonstiges
- Annealing HB : ≦202
- Quenching HRC : ≧65
Ländercode
- ASTM
Stahltyp
- W2A-91/2