ASTM-W1C-8
C(%) | Si(%) | Mn(%) | P(%) | S(%) | Ni(%) | Cr(%) | Mo(%) | W(%) | V(%) | Cu(%) |
---|---|---|---|---|---|---|---|---|---|---|
C(%)(%) 0,8-0,9 | Si(%)(%) 0,1-0,4 | Mn(%)(%) 0,1-0,4 | P(%)(%) ≦0,03 | S(%)(%) ≦0,03 | Ni(%)(%) ≦0,2 | Cr(%)(%) ≦0,3 | Mo(%)(%) ≦0.1 | W(%)(%) ≦0,15 | V(%)(%) ≦0.1 | Cu(%)(%) ≦0,2 |
Anwendungen
- Kohlenstoff-Werkzeugeisen
Sonstiges
- Annealing HB : ≦202
- Quenching HRC : ≧65
Ländercode
- ASTM
Stahltyp
- W1C-8
Stahltyp in Beziehung setzen
Stahltyp | Ländercode | Mehr | C80W1 | DIN | Mehr | C80W2 | DIN | Mehr | C85W2 | DIN | Mehr | T8MnA | GB | Mehr | SK5 | JIS | Mehr | SK6 | JIS | Mehr | W1A-8 | ASTM | Mehr | W1C-8 | ASTM | Mehr |
---|