ASTM-W1C-8
C(%) | Si(%) | Mn(%) | P(%) | S(%) | Ni (%) | Cr (%) | Mo (%) | W (%) | V(%) | Cu (%) |
---|---|---|---|---|---|---|---|---|---|---|
C(%)(%) 0,8-0,9 | Si(%)(%) 0,1-0,4 | Mn(%)(%) 0,1-0,4 | P(%)(%) ≦0,03 | S(%)(%) ≦0,03 | Ni (%)(%) ≦0,2 | Cr (%)(%) ≦0,3 | Mo (%)(%) ≦0.1 | W (%)(%) ≦0,15 | V(%)(%) ≦0.1 | Cu (%)(%) ≦0,2 |
Applications
- Aciers à outils en carbone
Autre
- Annealing HB : ≦202
- Quenching HRC : ≧65
Code pays
- ASTM
Type d'acier
- W1C-8