ASTM-W1A-8 1/2
C(%) | Si(%) | Mn(%) | P(%) | S(%) | Ni(%) | Cr(%) | Mo(%) | W(%) | V(%) | Cu(%) |
---|---|---|---|---|---|---|---|---|---|---|
C(%)(%) 0.85-0.95 | Si(%)(%) 0.1-0.4 | Mn(%)(%) 0.1-0.4 | P(%)(%) ≦0.03 | S(%)(%) ≦0.03 | Ni(%)(%) ≦0.2 | Cr(%)(%) ≦0.15 | Mo(%)(%) ≦0.1 | W(%)(%) ≦0.15 | V(%)(%) ≦0.1 | Cu(%)(%) ≦0.2 |
Aplicaciones
- Acero de herramientas de carbono
Otros
- Annealing HB : ≦202
- Quenching HRC : ≧65
Código de país
- ASTM
Tipo de acero
- W1A-8 1/2
Tipo de acero relacionado
Tipo de acero | Código de país | Más | T9 | GB | Más | W1A-8 1/2 | ASTM | Más | W1A-9 | ASTM | Más | W1C-9 | ASTM | Más | W2A-9 | ASTM | Más | W2C-9 | ASTM | Más | C85W2 | DIN | Más |
---|