ASTM-W1A-8 1/2
C(%) | Si(%) | Mn(%) | P(%) | S(%) | Ni(%) | Cr(%) | Mo(%) | W(%) | V(%) | Cu(%) |
---|---|---|---|---|---|---|---|---|---|---|
C(%)(%) 0.85-0.95 | Si(%)(%) 0.1-0.4 | Mn(%)(%) 0.1-0.4 | P(%)(%) ≦0.03 | S(%)(%) ≦0.03 | Ni(%)(%) ≦0.2 | Cr(%)(%) ≦0.15 | Mo(%)(%) ≦0.1 | W(%)(%) ≦0.15 | V(%)(%) ≦0.1 | Cu(%)(%) ≦0.2 |
Uygulamalar
- Karbon Alet Çelikleri
Diğer
- Annealing HB : ≦202
- Quenching HRC : ≧65
Ülke Kodu
- ASTM
Çelik Türü
- W1A-8 1/2
İlgili Çelik Türü
Çelik Türü | Ülke Kodu | Daha | T9 | GB | Daha | W1A-8 1/2 | ASTM | Daha | W1A-9 | ASTM | Daha | W1C-9 | ASTM | Daha | W2A-9 | ASTM | Daha | W2C-9 | ASTM | Daha | C85W2 | DIN | Daha |
---|