JIS-SCH13
C(%) | Si(%) | Mn(%) | P(%) | S(%) | Ni (%) | Cr (%) | Mo (%) | Contrainte de rendement (Mpa) | Contrainte de traction (Mpa) | Allongement (%) |
---|---|---|---|---|---|---|---|---|---|---|
C(%)(%) 0.2-0.5 | Si(%)(%) ≦2,0 | Mn(%)(%) ≦2,0 | P(%)(%) ≦0.04 | S(%)(%) ≦0.04 | Ni (%)(%) 11,0-14,0 | Cr (%)(%) 24,0-28,0 | Mo (%)(%) ≦0,5 | Contrainte de rendement (Mpa)(%) ≧235 | Contrainte de traction (Mpa)(%) ≧490 | Allongement (%)(%) ≧8 |
Applications
- Fonderies d'acier résistant à la chaleur
Code pays
- JIS
Norme
- G5122
Type d'acier
- SCH13