JIS-SCH16
C(%) | Si(%) | Mn(%) | P(%) | S(%) | Ni (%) | Cr (%) | Mo (%) | Contrainte de traction (Mpa) | Allongement (%) |
---|---|---|---|---|---|---|---|---|---|
C(%)(%) 0,20-0,35 | Si(%)(%) ≦2.5 | Mn(%)(%) ≦2,0 | P(%)(%) ≦0.04 | S(%)(%) ≦0.04 | Ni (%)(%) 33,0-37,0 | Cr (%)(%) 13,0-17,0 | Mo (%)(%) ≦0,5 | Contrainte de traction (Mpa)(%) ≧440 | Allongement (%)(%) ≧13 |
Applications
- Fonderies d'acier résistant à la chaleur