CNS-SCH13
C(%) | Si(%) | Mn(%) | P(%) | S(%) | Ni (%) | Cr (%) | Mo (%) | Vloeigrens (Mpa) | Treksterkte (Mpa) | Rekbaarheid (%) |
---|---|---|---|---|---|---|---|---|---|---|
C(%)(%) 0.2-0.5 | Si(%)(%) ≦2.0 | Mn(%)(%) ≦2.0 | P(%)(%) ≦0.04 | S(%)(%) ≦0.04 | Ni (%)(%) 11.0-14.0 | Cr (%)(%) 24.0-28.0 | Mo (%)(%) ≦0,5 | Vloeigrens (Mpa)(%) ≧235 | Treksterkte (Mpa)(%) ≧490 | Rekbaarheid (%)(%) ≧8 |
Toepassingen
- Hittestand staal gietstukken
Landcode
- CNS
Standaard
- 4002
Staaltype
- SCH13