ASTM-W2C-9
C(%) | Si(%) | Mn(%) | P(%) | S(%) | Ni(%) | Cr(%) | Mo(%) | W(%) | V(%) | Cu(%) |
---|---|---|---|---|---|---|---|---|---|---|
C(%)(%) 0.9-1.0 | Si(%)(%) 0.1-0.4 | Mn(%)(%) 0.1-0.4 | P(%)(%) ≦0.03 | S(%)(%) ≦0.03 | Ni(%)(%) ≦0.2 | Cr(%)(%) ≦0.3 | Mo(%)(%) ≦0.3 | W(%)(%) ≦0.15 | V(%)(%) 0.15-0.35 | Cu(%)(%) ≦0.2 |
Uygulamalar
- Karbon Alet Çelikleri
Diğer
- Sn : ≦0.05
- Annealing HB : ≦202
- Quenching HRC
Ülke Kodu
- ASTM
Çelik Türü
- W2C-9
İlgili Çelik Türü