JIS-SK4
C(%) | Si(%) | Mn(%) | P(%) | S(%) | Ni(%) | Cr(%) | Cu(%) |
---|---|---|---|---|---|---|---|
C(%)(%) 0.9-1.0 | Si(%)(%) 0.15-0.35 | Mn(%)(%) 0.15-0.5 | P(%)(%) ≦0.03 | S(%)(%) ≦0.03 | Ni(%)(%) ≦0.25 | Cr(%)(%) ≦0.3 | Cu(%)(%) ≦0.25 |
Ứng dụng
- Thép công cụ carbon
Khác
- Annealing HB : ≦207
- Quenching HRC : ≧61
Mã quốc gia
- JIS
Loại thép
- SK4
Loại thép liên quan