JIS-SUSF410D
C(%) | Si(%) | Mn(%) | P(%) | S(%) | Ni (%) | Cr (%) | Contrainte de rendement (Mpa) | Contrainte de traction (Mpa) | Allongement (%) |
---|---|---|---|---|---|---|---|---|---|
C(%)(%) ≦0,15 | Si(%)(%) ≦1.0 | Mn(%)(%) ≦1.0 | P(%)(%) ≦0.04 | S(%)(%) ≦0.04 | Ni (%)(%) ≦0,6 | Cr (%)(%) 11.5-13.5 | Contrainte de rendement (Mpa)(%) ≧760 | Contrainte de traction (Mpa)(%) ≧900 | Allongement (%)(%) ≧11 |
Applications
- Flasques/Accessoires/Robinetterie en acier inoxydable forgé et partie de récipients sous pression pour haute