JIS-SUSF410D
C(%) | Si(%) | Mn(%) | P(%) | S(%) | Ni(%) | Cr(%) | Tegangan Hasil (Mpa) | Tegangan Tarik (Mpa) | Elongasi (%) |
---|---|---|---|---|---|---|---|---|---|
C(%)(%) ≦0.15 | Si(%)(%) ≦1.0 | Mn(%)(%) ≦1.0 | P(%)(%) ≦0.04 | S(%)(%) ≦0.04 | Ni(%)(%) ≦0.6 | Cr(%)(%) 11.5-13.5 | Tegangan Hasil (Mpa)(%) ≧760 | Tegangan Tarik (Mpa)(%) ≧900 | Elongasi (%)(%) ≧11 |
Aplikasi
- Flens/Bahu/Katup Baja Tahan Karat yang Ditempa dan Bagian dari Wadah Tekanan untuk Tinggi
Kode Negara
- JIS
Standar
- G3214
Jenis Baja
- SUSF410D
Jenis Baja Terkait
Jenis Baja | Standar | Kode Negara | Lagi | F6A | A182 | ASTM | Lagi | F6 | A336 | ASTM | Lagi | SUSF410 | G3214 | JIS | Lagi | SUSF410B | G3214 | JIS | Lagi | SUSF410C | G3214 | JIS | Lagi | SUSF410D | G3214 | JIS | Lagi |
---|