ASTM-F11
C(%) | Si(%) | Mn(%) | P(%) | S(%) | Cr(%) | Mo(%) | Tegangan Hasil (Mpa) | Tegangan Tarik (Mpa) | Elongasi (%) |
---|---|---|---|---|---|---|---|---|---|
C(%)(%) 0.1-0.2 | Si(%)(%) 0.5-1.0 | Mn(%)(%) 0.3-0.8 | P(%)(%) ≦0.04 | S(%)(%) ≦0.04 | Cr(%)(%) 1.0-1.5 | Mo(%)(%) 0.45-0.65 | Tegangan Hasil (Mpa)(%) ≧275 | Tegangan Tarik (Mpa)(%) 485-650 | Elongasi (%)(%) ≧20 |
Aplikasi
- Paduan Baja Forging untuk Bejana Tekanan untuk Layanan Suhu Tinggi
Kode Negara
- ASTM
Jenis Baja
- F11
Jenis Baja Terkait
Pertanyaan | Jenis Baja | Kode Negara | Lagi | SFVA-F11A | CNS | Lagi | 15CrMo | GB | Lagi | SFVA-F11A | JIS | Lagi | F11 Class 2 | ASTM | Lagi | F11 | ASTM | Lagi | 13CrMo-4-4 | DIN | Lagi |
---|