ASTM-F304
C(%) | Si(%) | Mn(%) | P(%) | S(%) | Ni(%) | Cr(%) | Tegangan Hasil (Mpa) | Tegangan Tarik (Mpa) | Elongasi (%) |
---|---|---|---|---|---|---|---|---|---|
C(%)(%) ≦0.08 | Si(%)(%) ≦1.0 | Mn(%)(%) ≦2.0 | P(%)(%) ≦0.045 | S(%)(%) -0.03 | Ni(%)(%) 8.0-11.0 | Cr(%)(%) 18.0-20.0 | Tegangan Hasil (Mpa)(%) ≧207 | Tegangan Tarik (Mpa)(%) ≧515 | Elongasi (%)(%) ≧30 |
Aplikasi
- Flens/Bahu/Katup Baja Tahan Karat yang Ditempa dan Bagian dari Wadah Tekanan untuk Tinggi
Kode Negara
- ASTM
Standar
- A182
Jenis Baja
- F304
Jenis Baja Terkait
Jenis Baja | Standar | Kode Negara | Lagi | F304 | 8702 | CNS | Lagi | SUSF304 | G3214 | JIS | Lagi | F304 | A182 | ASTM | Lagi | F304 | A336 | ASTM | Lagi | X5CrNi-18-10 | 17440 | DIN | Lagi |
---|