ASTM-F304H
C(%) | Si(%) | Mn(%) | P(%) | S(%) | Ni(%) | Cr(%) | Tegangan Hasil (Mpa) | Tegangan Tarik (Mpa) | Elongasi (%) |
---|---|---|---|---|---|---|---|---|---|
C(%)(%) 0.04-0.10 | Si(%)(%) ≦1.0 | Mn(%)(%) ≦2.0 | P(%)(%) ≦0.04 | S(%)(%) ≦0.03 | Ni(%)(%) 8.0-12.0 | Cr(%)(%) 19.0-20.0 | Tegangan Hasil (Mpa)(%) ≧205 | Tegangan Tarik (Mpa)(%) ≧485 | Elongasi (%)(%) ≧30 |
Aplikasi
- Flens/Bahu/Katup Baja Tahan Karat yang Ditempa dan Bagian dari Wadah Tekanan untuk Tinggi
Kode Negara
- ASTM
Standar
- A336
Jenis Baja
- F304H
Jenis Baja Terkait
Jenis Baja | Standar | Kode Negara | Lagi | F304H | 8702 | CNS | Lagi | SUS304H | G3214 | JIS | Lagi | F304H | A182 | ASTM | Lagi | F304H | A336 | ASTM | Lagi |
---|