ASTM-F316H
C(%) | Si(%) | Mn(%) | P(%) | S(%) | Ni(%) | Cr(%) | Mo(%) | Tegangan Hasil (Mpa) | Tegangan Tarik (Mpa) | Elongasi (%) |
---|---|---|---|---|---|---|---|---|---|---|
C(%)(%) 0.04-0.10 | Si(%)(%) ≦1.0 | Mn(%)(%) ≦2.0 | P(%)(%) ≦0.045 | S(%)(%) ≦0.03 | Ni(%)(%) 10.0-14.0 | Cr(%)(%) 16.0-18.0 | Mo(%)(%) 2.0-3.0 | Tegangan Hasil (Mpa)(%) ≧205 | Tegangan Tarik (Mpa)(%) ≧485 | Elongasi (%)(%) ≧30 |
Aplikasi
- Flens/Bahu/Katup Baja Tahan Karat yang Ditempa dan Bagian dari Wadah Tekanan untuk Tinggi
Kode Negara
- ASTM
Standar
- A336
Jenis Baja
- F316H
Jenis Baja Terkait
Jenis Baja | Standar | Kode Negara | Lagi | F316H | 8702 | CNS | Lagi | SUS316H | G3214 | JIS | Lagi | F316H | A182 | ASTM | Lagi | F316H | A336 | ASTM | Lagi |
---|