ASTM-F316L
C(%) | Si(%) | Mn(%) | P(%) | S(%) | Ni(%) | Cr(%) | Mo(%) | Tegangan Hasil (Mpa) | Tegangan Tarik (Mpa) | Elongasi (%) |
---|---|---|---|---|---|---|---|---|---|---|
C(%)(%) ≦0.035 | Si(%)(%) ≦1.0 | Mn(%)(%) ≦2.0 | P(%)(%) ≦0.04 | S(%)(%) ≦0.03 | Ni(%)(%) 10.0-15.0 | Cr(%)(%) 16.0-18.0 | Mo(%)(%) 2.0-3.0 | Tegangan Hasil (Mpa)(%) ≧170 | Tegangan Tarik (Mpa)(%) ≧150 | Elongasi (%)(%) ≧30 |