ASTM-Gr.WC9
C(%) | Si(%) | Mn(%) | P(%) | S(%) | Ni(%) | Cr(%) | Mo(%) | W(%) | Cu(%) | Tegangan Hasil (Mpa) | Tegangan Tarik (Mpa) | Elongasi (%) |
---|---|---|---|---|---|---|---|---|---|---|---|---|
C(%)(%) 0.05-0.18 | Si(%)(%) ≦0.6 | Mn(%)(%) 0.4-0.7 | P(%)(%) ≦0.04 | S(%)(%) ≦0.045 | Ni(%)(%) ≦0.5 | Cr(%)(%) 2.00-2.75 | Mo(%)(%) 0.9-1.2 | W(%)(%) ≦0.1 | Cu(%)(%) ≦0.5 | Tegangan Hasil (Mpa)(%) ≧275 | Tegangan Tarik (Mpa)(%) 485-655 | Elongasi (%)(%) ≧40 |
Aplikasi
- Paduan Baja Cor untuk Layanan Suhu Tinggi dan Tekanan Tinggi
Kode Negara
- ASTM
Standar
- A217
Jenis Baja
- Gr.WC9
Jenis Baja Terkait
Jenis Baja | Standar | Kode Negara | Lagi | SCPH32 | G5151 | JIS | Lagi | Gr.WC9 | A217 | ASTM | Lagi | SCPH32 | 7147 | CNS | Lagi | ZG12Cr2-Mo1G | 16253 | GB | Lagi | GS-18Cr-Mo9-10 | 17245 | JIS | Lagi |
---|