ASTM-LF3
C(%) | Si(%) | Mn(%) | P(%) | S(%) | Ni(%) | Cr(%) | Mo(%) | V(%) | Cu(%) | Tegangan Hasil (Mpa) | Tegangan Tarik (Mpa) |
---|---|---|---|---|---|---|---|---|---|---|---|
C(%)(%) ≦0.2 | Si(%)(%) 0.20-0.35 | Mn(%)(%) ≦0.9 | P(%)(%) ≦0.035 | S(%)(%) ≦0.04 | Ni(%)(%) 3.25-3.75 | Cr(%)(%) ≦0.3 | Mo(%)(%) ≦0.12 | V(%)(%) ≦0.03 | Cu(%)(%) ≦0.4 | Tegangan Hasil (Mpa)(%) ≧260 | Tegangan Tarik (Mpa)(%) 485-655 |
Aplikasi
- Paduan Karbon dan Baja untuk Pengecoran Wadah Tekanan untuk Layanan Suhu Rendah
Lainnya
- Nb : ≦0.02
Kode Negara
- ASTM
Standar
- A350
Jenis Baja
- LF3
Jenis Baja Terkait
Jenis Baja | Standar | Kode Negara | Lagi | SFL3 | G3205 | JIS | Lagi | LF3 | A350 | ASTM | Lagi | 10Nil14 | DIN | Lagi | SFL3 | 11067 | CNS | Lagi |
---|