CNS-F304L
C(%) | Si(%) | Mn(%) | P(%) | S(%) | Ni(%) | Cr(%) | Tebal (mm) | Tegangan Hasil (Mpa) | Tegangan Tarik (Mpa) | Elongasi (%) |
---|---|---|---|---|---|---|---|---|---|---|
C(%)(%) ≦0.03 | Si(%)(%) ≦1.0 | Mn(%)(%) ≦2.0 | P(%)(%) ≦0.04 | S(%)(%) ≦0.03 | Ni(%)(%) 9.0-13.0 | Cr(%)(%) 18.0-20.0 | Tebal (mm)(%) ≦130 | Tegangan Hasil (Mpa)(%) ≧175 | Tegangan Tarik (Mpa)(%) ≧480 | Elongasi (%)(%) ≧29 |
Aplikasi
- Flens/Bahu/Katup Baja Tahan Karat yang Ditempa dan Bagian dari Wadah Tekanan untuk Tinggi
Kode Negara
- CNS
Standar
- 8702
Jenis Baja
- F304L
Jenis Baja Terkait