CNS-F316
C(%) | Si(%) | Mn(%) | P(%) | S(%) | Ni(%) | Cr(%) | Mo(%) | Tebal (mm) | Tegangan Hasil (Mpa) | Tegangan Tarik (Mpa) | Elongasi (%) |
---|---|---|---|---|---|---|---|---|---|---|---|
C(%)(%) ≦0.08 | Si(%)(%) ≦1.0 | Mn(%)(%) ≦2.0 | P(%)(%) ≦0.04 | S(%)(%) ≦0.03 | Ni(%)(%) 10.0-14.0 | Cr(%)(%) 16.0-18.0 | Mo(%)(%) 2.0-3.0 | Tebal (mm)(%) ≦130 | Tegangan Hasil (Mpa)(%) ≧205 | Tegangan Tarik (Mpa)(%) ≧520 | Elongasi (%)(%) ≧43 |
Aplikasi
- Flens/Bahu/Katup Baja Tahan Karat yang Ditempa dan Bagian dari Wadah Tekanan untuk Tinggi
Kode Negara
- CNS
Standar
- 8702
Jenis Baja
- F316
Jenis Baja Terkait
Jenis Baja | Standar | Kode Negara | Lagi | F316 | 8702 | CNS | Lagi | SUSF316 | G3214 | JIS | Lagi | F316 | A182 | ASTM | Lagi | F316 | A336 | ASTM | Lagi | X5CrNi-Mo17-12-2 | 17440 | DIN | Lagi |
---|