DIN-32Cr-Mo12
C(%) | Si(%) | Mn(%) | P(%) | S(%) | Cr(%) | Mo(%) | Tegangan Hasil (Mpa) | Tegangan Tarik (Mpa) | Elongasi (%) |
---|---|---|---|---|---|---|---|---|---|
C(%)(%) 0.28-0.35 | Si(%)(%) 0.15-0.40 | Mn(%)(%) 0.4-0.7 | P(%)(%) ≦0.035 | S(%)(%) ≦0.035 | Cr(%)(%) 2.8-3.0 | Mo(%)(%) 0.3-0.5 | Tegangan Hasil (Mpa)(%) ≧785 | Tegangan Tarik (Mpa)(%) 980-1180 | Elongasi (%)(%) ≧11 |
Aplikasi
- Paduan Baja Forging untuk Bejana Tekanan untuk Layanan Suhu Tinggi
Kode Negara
- DIN
Jenis Baja
- 32Cr-Mo12