JIS-SCMnCr-M3B
C(%) | Si(%) | Mn(%) | P(%) | S(%) | Cr(%) | Mo(%) | Tegangan Hasil (Mpa) | Tegangan Tarik (Mpa) | Elongasi (%) |
---|---|---|---|---|---|---|---|---|---|
C(%)(%) 0.3-0.4 | Si(%)(%) 0.3-0.6 | Mn(%)(%) 1,2-1,6 | P(%)(%) ≦0.04 | S(%)(%) ≦0.04 | Cr(%)(%) 0.3-0.7 | Mo(%)(%) 0.15-0.35 | Tegangan Hasil (Mpa)(%) ≧635 | Tegangan Tarik (Mpa)(%) ≧830 | Elongasi (%)(%) ≧9 |
Aplikasi
- Paduan Baja Karbon dengan Kekuatan Tarik Tinggi dan Paduan Baja Low Alloy untuk Struktur
Kode Negara
- JIS
Standar
- G5111
Jenis Baja
- SCMnCr-M3B
Jenis Baja Terkait
Jenis Baja | Standar | Kode Negara | Lagi |
SCMnCr-M3B |
7145 | CNS | Lagi |
SCMnCr-M3B |
G5111 | JIS | Lagi |
115-95 |
A148 | ASTM | Lagi |
---|