JIS-SCPH2
C(%) | Si(%) | Mn(%) | P(%) | S(%) | Ni(%) | Cr(%) | Mo(%) | Cu(%) | Tegangan Hasil (Mpa) | Tegangan Tarik (Mpa) | Elongasi (%) |
---|---|---|---|---|---|---|---|---|---|---|---|
C(%)(%) ≦0.3 | Si(%)(%) ≦0.6 | Mn(%)(%) ≦1.0 | P(%)(%) ≦0.04 | S(%)(%) ≦0.04 | Ni(%)(%) ≦0.5 | Cr(%)(%) ≦0.25 | Mo(%)(%) ≦0.25 | Cu(%)(%) ≦0.5 | Tegangan Hasil (Mpa)(%) ≧245 | Tegangan Tarik (Mpa)(%) ≧480 | Elongasi (%)(%) ≧19 |
Aplikasi
- Paduan Baja Cor untuk Layanan Suhu Tinggi dan Tekanan Tinggi
Kode Negara
- JIS
Standar
- G5151
Jenis Baja
- SCPH2
Jenis Baja Terkait
Jenis Baja | Standar | Kode Negara | Lagi | SCPH2 | 7147 | CNS | Lagi | ZG280-520 | 16253 | GB | Lagi | SCPH2 | G5151 | JIS | Lagi | Gr.WCB | A216 | ASTM | Lagi |
---|