JIS-SQV2A
C(%) | Si(%) | Mn(%) | P(%) | S(%) | Ni(%) | Mo(%) | Tegangan Hasil (Mpa) | Tegangan Tarik (Mpa) | Elongasi (%) |
---|---|---|---|---|---|---|---|---|---|
C(%)(%) ≦0.25 | Si(%)(%) 0.15-0.30 | Mn(%)(%) 1.15-1.50 | P(%)(%) ≦0.035 | S(%)(%) ≦0.04 | Ni(%)(%) 0.4-0.7 | Mo(%)(%) 0.45-0.60 | Tegangan Hasil (Mpa)(%) ≧345 | Tegangan Tarik (Mpa)(%) 550-690 | Elongasi (%)(%) ≧18 |
Aplikasi
- Pelat Baja Paduan Mn-Mo dan Mn-Mo-Ni yang Dikuatkan dan Ditemper untuk Wadah Tekanan
Kode Negara
- JIS
Standar
- G3120
Jenis Baja
- SQV2A
Jenis Baja Terkait
Jenis Baja | Standar | Kode Negara | Lagi |
SQV2A |
8973 | CNS | Lagi |
SQV2A |
G3120 | JIS | Lagi |
Type B Class 1 |
A533 | ASTM | Lagi |
20MnMoNi55 |
SEW-640 | DIN | Lagi |
---|