C(%) | Si(%) | Mn(%) | P(%) | S(%) | Ni(%) | Cr(%) | Mo(%) | V(%) | Tegangan Hasil (Mpa) | Tegangan Tarik (Mpa) | Pemanjangan (%) |
---|---|---|---|---|---|---|---|---|---|---|---|
C(%)(%) ≦0.25 | Si(%)(%) 0.15-0.35 | Mn(%)(%) 1.2-1.5 | P(%)(%) ≦0.025 | S(%)(%) ≦0.025 | Ni(%)(%) 0.4-1.0 | Cr(%)(%) ≦0.25 | Mo(%)(%) 0.45-0.60 | V(%)(%) ≦0.05 | Tegangan Hasil (Mpa)(%) ≧450 | Tegangan Tarik (Mpa)(%) 620-790 | Pemanjangan (%)(%) ≧16 |
Aplikasi
- Paduan Keluli yang Didinginkan dan Ditemper untuk Bekas Tekanan