C(%) | Si(%) | Mn(%) | P(%) | S(%) | Ni(%) | Cr(%) | Ti(%) | Tegangan Hasil (Mpa) | Tegangan Tarik (Mpa) |
---|---|---|---|---|---|---|---|---|---|
C(%)(%) ≦0.08 | Si(%)(%) ≦0.85 | Mn(%)(%) ≦2.5 | P(%)(%) ≦0.035 | S(%)(%) ≦0.03 | Ni(%)(%) ≧9.0 | Cr(%)(%) ≧17.0 | Ti(%)(%) 5xC%-0.6 | Tegangan Hasil (Mpa)(%) ≧205 | Tegangan Tarik (Mpa)(%) ≧485 |
Aplikasi
- Flange/Fitting/Valve Keluli Tahan Karat yang Ditempa dan Bahagian Bekas Tekanan untuk Tinggi
Kod Negara
- ASTM
Standard
- A336
Jenis Baja
- F321