ASTM-F347
C(%) | Si(%) | Mn(%) | P(%) | S(%) | Ni(%) | Cr(%) | Tegangan Hasil (Mpa) | Tegangan Tarik (Mpa) | Pemanjangan (%) |
---|---|---|---|---|---|---|---|---|---|
C(%)(%) ≦0.08 | Si(%)(%) ≦1.0 | Mn(%)(%) ≦2.0 | P(%)(%) ≦0.04 | S(%)(%) ≦0.03 | Ni(%)(%) 9.0-12.0 | Cr(%)(%) 17.0-19.0 | Tegangan Hasil (Mpa)(%) ≧205 | Tegangan Tarik (Mpa)(%) ≧515 | Pemanjangan (%)(%) ≧30 |
Aplikasi
- Flange/Fitting/Valve Keluli Tahan Karat yang Ditempa dan Bahagian Bekas Tekanan untuk Tinggi
Kod Negara
- ASTM
Standard
- A182
Jenis Baja
- F347
Jenis Baja yang Berkaitan
Jenis Baja | Standard | Kod Negara | More |
F347 |
8702 | CNS | More |
SUSF347 |
G3214 | JIS | More |
F347 |
A182 | ASTM | More |
F347 |
A336 | ASTM | More |
X6CrNI-Nb18-10 |
17440 | DIN | More |
---|