ASTM-F5A
C(%) | Si(%) | Mn(%) | P(%) | S(%) | Ni(%) | Cr(%) | Mo(%) | Tegangan Hasil (Mpa) | Tegangan Tarik (Mpa) | Pemanjangan (%) |
---|---|---|---|---|---|---|---|---|---|---|
C(%)(%) ≦0.25 | Si(%)(%) ≦0.5 | Mn(%)(%) ≦0.6 | P(%)(%) ≦0.04 | S(%)(%) ≦0.03 | Ni(%)(%) ≦0.5 | Cr(%)(%) 4.0-6.0 | Mo(%)(%) 0.44-0.65 | Tegangan Hasil (Mpa)(%) ≧450 | Tegangan Tarik (Mpa)(%) ≧620 | Pemanjangan (%)(%) ≧22 |
Aplikasi
- Paduan Keluli Forging untuk Bekas Tekanan untuk Perkhidmatan Suhu Tinggi
Kod Negara
- ASTM
Jenis Baja
- F5A