ASTM-Gr.A
C(%) | Si(%) | Mn(%) | P(%) | S(%) | Ni(%) | Cr(%) | V(%) | Cu(%) | Tebal (mm) | Tegangan Hasil (Mpa) | Tegangan Tarik (Mpa) | Pemanjangan (%) |
---|---|---|---|---|---|---|---|---|---|---|---|---|
C(%)(%) ≦0.19 | Si(%)(%) 0.30-0.65 | Mn(%)(%) 0.80-1.25 | P(%)(%) ≦0.04 | S(%)(%) ≦0.05 | Ni(%)(%) ≦0.40 | Cr(%)(%) 0.40-0.65 | V(%)(%) 0.02-0.10 | Cu(%)(%) 0.25-0.40 | Tebal (mm)(%) ≦100 | Tegangan Hasil (Mpa)(%) ≧345 | Tegangan Tarik (Mpa)(%) ≧485 | Pemanjangan (%)(%) ≧21 |
Aplikasi
- Keluli Tahan Karat yang Dihasilkan Secara Panas untuk Struktur Las
Kod Negara
- ASTM
Standard
- A588M
Jenis Baja
- Gr.A
Jenis Baja yang Berkaitan
Jenis Baja | Standard | Kod Negara | More |
SMA400AP |
4269 | CNS | More |
SMA400AP |
G3114 | JIS | More |
Gr.A |
A588M | ASTM | More |
---|