ASTM-Gr.WCB
C(%) | Si(%) | Mn(%) | P(%) | S(%) | Ni(%) | Cr(%) | Mo(%) | Cu(%) | Tegangan Hasil (Mpa) | Tegangan Tarik (Mpa) | Pemanjangan (%) |
---|---|---|---|---|---|---|---|---|---|---|---|
C(%)(%) ≦0.3 | Si(%)(%) ≦0.6 | Mn(%)(%) ≦1.0 | P(%)(%) ≦0.04 | S(%)(%) ≦0.045 | Ni(%)(%) ≦0.5 | Cr(%)(%) ≦0.5 | Mo(%)(%) ≦0.2 | Cu(%)(%) ≦0.3 | Tegangan Hasil (Mpa)(%) ≧250 | Tegangan Tarik (Mpa)(%) 485-655 | Pemanjangan (%)(%) ≧22 |
Aplikasi
- Tuangan Keluli untuk Perkhidmatan Suhu Tinggi dan Tekanan Tinggi
- Pengecoran Keluli untuk Struktur Las