CNS-NCF80A
C(%) | Si(%) | Mn(%) | P(%) | S(%) | Cr(%) | Cu(%) | Al(%) | Ti(%) | Fe(%) | Tebal (mm) | Tegangan Hasil (Mpa) | Tegangan Tarik (Mpa) | Pemanjangan (%) |
---|---|---|---|---|---|---|---|---|---|---|---|---|---|
C(%)(%) 0.04-0.10 | Si(%)(%) ≦1.0 | Mn(%)(%) ≦1.0 | P(%)(%) ≦0.03 | S(%)(%) ≦0.015 | Cr(%)(%) 18.0-21.0 | Cu(%)(%) ≦0.2 | Al(%)(%) 1.0-1.8 | Ti(%)(%) 1.0-1.8 | Fe(%)(%) ≦1.5 | Tebal (mm)(%) -≦600 | Tegangan Hasil (Mpa)(%) ≧635 | Tegangan Tarik (Mpa)(%) ≧1000 | Pemanjangan (%)(%) ≧20 |
Aplikasi
- Lembaran, Plat dan Bar Superalloy Tahan Karat dan Tahan Panas
Kod Negara
- CNS
Jenis Baja
- NCF80A
Jenis Baja yang Berkaitan
Jenis Baja | Kod Negara | More |
NCF80A |
CNS | More |
GH80A |
GB | More |
NCF80A |
JIS | More |
NiCr20Ti-A1 |
DIN | More |
---|