CNS-SCMnCr-M3B
C(%) | Si(%) | Mn(%) | P(%) | S(%) | Cr(%) | Mo(%) | Tegangan Hasil (Mpa) | Tegangan Tarik (Mpa) | Pemanjangan (%) |
---|---|---|---|---|---|---|---|---|---|
C(%)(%) 0.3-0.4 | Si(%)(%) 0.3-0.6 | Mn(%)(%) 1.2-1.6 | P(%)(%) ≦0.04 | S(%)(%) ≦0.04 | Cr(%)(%) 0.3-0.7 | Mo(%)(%) 0.15-0.35 | Tegangan Hasil (Mpa)(%) ≧635 | Tegangan Tarik (Mpa)(%) ≧830 | Pemanjangan (%)(%) ≧9 |
Aplikasi
- Pengecoran Keluli Karbon Kekuatan Tegangan Tinggi dan Pengecoran Keluli Aloi Rendah untuk Struktur
Kod Negara
- CNS
Standard
- 7145
Jenis Baja
- SCMnCr-M3B
Jenis Baja yang Berkaitan
Jenis Baja | Standard | Kod Negara | More |
SCMnCr-M3B |
7145 | CNS | More |
SCMnCr-M3B |
G5111 | JIS | More |
115-95 |
A148 | ASTM | More |
---|