DIN-34CrA1S5
C(%) | Si(%) | Mn(%) | P(%) | S(%) | Ni(%) | Mo(%) | Tebal (mm) | Tegangan Hasil (Mpa) | Tegangan Tarik (Mpa) | Pemanjangan (%) |
---|---|---|---|---|---|---|---|---|---|---|
C(%)(%) 0.30-0.37 | Si(%)(%) 0.15-0.40 | Mn(%)(%) 0.6-0.9 | P(%)(%) ≦0.03 | S(%)(%) ≦0.035 | Ni(%)(%) 1.0-1.3 | Mo(%)(%) 0.8-1.2 | Tebal (mm)(%) ≦60 | Tegangan Hasil (Mpa)(%) ≧440 | Tegangan Tarik (Mpa)(%) 640-790 | Pemanjangan (%)(%) ≧12 |
Aplikasi
- Keluli Aluminium Kromium Molybdenum untuk penggunaan Struktur Mesin
Kod Negara
- DIN
Standard
- 17211
Jenis Baja
- 34CrA1S5
Jenis Baja yang Berkaitan
Jenis Baja | Standard | Kod Negara | More | Class B | A355 | ASTM | More | 34CrA1S5 | 17211 | DIN | More |
---|