C(%) | Si(%) | Mn(%) | P(%) | S(%) | Ni(%) | Cr(%) | Mo(%) | Tebal (mm) | Tegangan Hasil (Mpa) | Tegangan Tarik (Mpa) | Pemanjangan (%) |
---|---|---|---|---|---|---|---|---|---|---|---|
C(%)(%) 0.30-0.27 | Si(%)(%) 0.2-0.5 | Mn(%)(%) 0.5-0.8 | P(%)(%) ≦0.03 | S(%)(%) ≦0.035 | Ni(%)(%) 1.0-1.3 | Cr(%)(%) 0.15-0.25 | Mo(%)(%) 0.8-1.2 | Tebal (mm)(%) ≦70 | Tegangan Hasil (Mpa)(%) ≧590 | Tegangan Tarik (Mpa)(%) 780-980 | Pemanjangan (%)(%) ≧14 |
Aplikasi
- Keluli Aluminium Kromium Molybdenum untuk penggunaan Struktur Mesin