DIN-GS-60
C(%) | Si(%) | Mn(%) | P(%) | S(%) | Tegangan Hasil (Mpa) | Tegangan Tarik (Mpa) | Pemanjangan (%) |
---|---|---|---|---|---|---|---|
C(%)(%) 0.4-0.4 | Si(%)(%) 0.3-0.6 | Mn(%)(%) 0.2-0.5 | P(%)(%) ≦0.04 | S(%)(%) ≦0.04 | Tegangan Hasil (Mpa)(%) ≧300 | Tegangan Tarik (Mpa)(%) ≧600 | Pemanjangan (%)(%) ≧15 |
Aplikasi
- Pengecoran Keluli Karbon Kekuatan Tegangan Tinggi dan Pengecoran Keluli Aloi Rendah untuk Struktur