DIN-X5CrNi-18-10
C(%) | Si(%) | Mn(%) | P(%) | S(%) | Ni(%) | Cr(%) | Tegangan Hasil (Mpa) | Tegangan Tarik (Mpa) | Pemanjangan (%) |
---|---|---|---|---|---|---|---|---|---|
C(%)(%) ≦0.07 | Si(%)(%) ≦1.0 | Mn(%)(%) ≦2.0 | P(%)(%) ≦0.045 | S(%)(%) ≦0.015 | Ni(%)(%) 11.0-13.0 | Cr(%)(%) 17.0-19.0 | Tegangan Hasil (Mpa)(%) ≧185 | Tegangan Tarik (Mpa)(%) 500-700 | Pemanjangan (%)(%) ≧50 |
Aplikasi
- Flange/Fitting/Valve Keluli Tahan Karat yang Ditempa dan Bahagian Bekas Tekanan untuk Tinggi
Kod Negara
- DIN
Standard
- 17440
Jenis Baja
- X5CrNi-18-10
Jenis Baja yang Berkaitan
Jenis Baja | Standard | Kod Negara | More | F304 | 8702 | CNS | More | SUSF304 | G3214 | JIS | More | F304 | A182 | ASTM | More | F304 | A336 | ASTM | More | X5CrNi-18-10 | 17440 | DIN | More |
---|